拉伸强度 | ASTM D638/ISO 527 | 61 | kg/cm²(MPa)[Lb/in²] | |
洛氏硬度 | ASTM D785 | 80 | ||
弯曲模量 | ASTM D790/ISO 178 | 2600 | kg/cm²(MPa)[Lb/in²] | |
弯曲强度 | ASTM D790/ISO 178 | 88 | kg/cm²(MPa)[Lb/in²] | |
IZOD 缺口冲击强度 | ASTM D256/ISO 179 | 59 | kg·cm/cm(J/M)ft·lb/in | |
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 60 | % | |
热变形温度 | ASTM D648/ISO 75 | 158 | ℃(℉) | |
ASTM D648/ISO 75 | 110 | ℃(℉) | ||
成型收缩率 | ASTM D955 | 1.6-2.0 | % | |
密度 | ASTM D792/ISO 1183 | 1.41 | ||
熔融指数(流动系数) | ASTM D1238/ISO 1133 | 9 | g/10min | |
吸水率 23℃/24H | ASTM D570/ISO 62 | 0.2 | % |