1.8-2.0%机械性能测试条件测试方法测试结果单位埃佐冲击试验缺口-40℃ASTM D-25655J/m23℃ASTM D-25671J/m无缺口23℃ASTM D-2561620J/m弹性系数23℃ASTM D-6383640Mpa负载变形量140kg/cm2,50℃ASTM D-6210.5%抗剪强度23℃ASTM D-73266Mpa抗拉伸冲击强度23℃ASTM D-1822250kJ/m²拉伸强度-55℃ASTM D-638101Mpa100℃ASTM D-63836Mpa23℃ASTM D-63869Mpa70℃ASTM D-63848Mpa122℃ASTM D-63826Mpa洛氏硬度M
ASTM D-78594
洛氏硬度R
ASTM D-785120
挠曲变形强度23℃ASTM D-79097Mpa挠曲疲劳忍耐限度50%RH，23℃，106周期ASTM D-67132Mpa挠曲系数122℃ASTM D-790755Mpa-55℃ASTM D-7904730Mpa70℃ASTM D-7901720Mpa100℃ASTM D-7901030Mpa23℃ASTM D-7903220Mpa破裂点拉伸变形量100℃ASTM D-638>260%122℃ASTM D-638>260%-55℃ASTM D-63810%23℃ASTM D-63825%70℃ASTM D-638180%压缩应力23℃，10%变形ASTM D-695121Mpa23℃，1%变形ASTM D-69535Mpa热性能测试条件测试方法测试结果单位热传导系数
0.37w/mk热畸变温度1.8MPaASTM D-648136
熔点
ASTM D-2133175
线性热膨胀系数104-160℃ASTM D-69614.910-5m/m60-104℃ASTM D-69613.710-5m/m29-60℃ASTM D-69612.210-5m/m-40-29ASTM D-69610.410-5m/m自燃性
UL 94HB
电气性能测试条件测试方法测试结果单位介电常数50%RH，23℃，102-106HzASTM D-1503.7ohm-cm介电强度2.3mmASTM D-14919.7KV/mm介电因数50%RH，23℃，106HzASTM D-1500.005
抗电弧3.1mmASTM D-495220sec容积电阻率23℃，0.2%含水量ASTM D-257≥14.9ohm-cm基本性能测试条件测试方法测试结果单位吸水率50%相对湿度ASTM D-5700.22%浸渍平衡点ASTM D-5700.90%24小时浸渍ASTM D-5700.25%